SpecificationASTM A182
304H
The 304H alloy is an improved version of 304 with a carbon content between 0.04-0.10. For parts that will be exposed to a temperature higher than 800°F, the use of 304H helps improve the strength at high temperatures.
Quick Navigation
Inquiry
Specifications
Chemical composition (wt. %)
Element
C
Si
Mn
P
S
Ni
Cr
Mo
N
Min.
0.04
-
-
-
-
8.00
18.00
-
-
Max.
0.10
1.00
2.00
0.040
0.030
10.50
20.00
1.00
0.10
Physical Property
Density (g/cm^3)
7.9
Modulus of elasticity
Temperature (℃)
Gpa
20
200
Thermal Expansion Coefficient
Temperature (℃)
10^-6/℃
20~100
16.6
Mechanical Property
Items
Solution
Tensile Strength Rm (KSI)
75 min.
Hardness (HBW)
223 max.
Yield Strength 0.2%Rp (KSI)
30 min.
Percentage of Elongation A(%)
40 min.
Size Ranges
Products
Diameter (mm)
Length (mm)
Rolled bar
10~95
3,000~5,700
Forged bar
95.2~440
3,000~5,700
Billet
130x130, 140x140, 150x150, 160x160
7,000 max.
Flat bar
80x80 (min.)
Based on the customer needs
Heat Treatment Conditions
Heat Treatment Conditions
Solution Treatment: 1040℃, water cooling