13-8Mo/1.4534/S13800/XM-13 | Precipitation Hardening Stainless Steel

13-8Mo

1.4534, S13800

SpecificationASTM A564/A564M、AMS 5629

It is a hardened stainless steel that has high strength as well as hardness, good corrosion resistance, and stress cracking resistance.

Quick Navigation

Introduction
Specifications

Inquiry

Introduction

Product properties

˙Good stress resistance

˙Corrosion Cracking resistance

Industrial Applications

˙Aerospace

˙Energy

˙Industrial devices

Specifications

Chemical composition (wt. %)

Element

Min.

7.50

12.25

2.00

0.90

Max.

0.05

0.10

0.010

0.008

8.50

13.25

2.50

1.35

0.01

Physical Property

Density (g/cm^3)

7.8

Modulus of elasticity

Temperature (℃)

Gpa

230

Thermal Expansion Coefficient

Temperature (℃)

10^-6/℃

100

10.6

Thermal Conductivity

Temperature (℃)

W/m·K

100

Mechanical Property

Items

Solution

H900

H925

H1025

H1050

H1100

Hardness (HRC)

38 max.

45 min.

43 min.

41 min.

40 min.

34 min.

Tensile Strength Rm (KSI)

220 min.

205 min.

185 min.

175 min.

150 min.

Yield Strength 0.2%Rp (KSI)

205 min.

190 min.

175 min.

165 min.

135 min.

Percentage of Elongation A(%)

10 min.

11 min.

12 min.

14 min.

Section Shrinkage Z(%)

45 min.

50 min.

Size Ranges

Products

Diameter (mm)

Length (mm)

Rolled bar

10~95

3,000~5,700

Forged bar

95.2~245

3,000~5,700

Billet

130x130, 140x140, 150x150, 160x160

7,000 max

Flat bar

80x80 (min.)

Based on the customer needs

The product has been added to the inquiry form!

Precipitation Hardening Stainless Steel 13-8Mo/1.4534/S13800/XM-13 – GMTC

13-8Mo

Product properties

Industrial Applications

Newsletter Subscription