Precipitation Hardening Stainless Steel 630/17-4PH/1.4542/X5CrNiCuNb16-4/S17400 (solution,H900~HH1150) – GMTC

630

  • 1.4542, S17400, SUS 630

SpecificationDIN EN 10088, ASTM A564/A564M, AMS 5643, JIS G4303

It is also known as 17-4 because of its strength and hardness after precipitation heat treatment.

Quick Navigation

Inquiry

Introduction

Product properties

˙High strength

˙High hardness

˙Good corrosion resistance

Industrial Applications

˙Biomedical instruments

˙Actutors

˙Energy

Specifications

Chemical composition (wt. %)

Element
C
Si
Mn
P
S
Ni
Cr
Mo
Cu
Nb
Min.
-
-
-
-
-
3.00
15.00
-
3.00
5xC
Max.
0.07
1.00
1.00
0.040
0.030
5.00
17.50
0.50
5.00
0.45

Physical Property

Density (g/cm^3)
7.75

Modulus of elasticity

Temperature (℃)
Gpa
20
200

Thermal Expansion Coefficient

Temperature (℃)
10^-6/℃
100
10.9
300
11.1

Thermal Conductivity

Temperature (℃)
W/m·K
20
16

Mechanical Property

Items
Solution
H900
H925
H1025
H1075
H1100
H1150
HH1150
Hardness (HRC)
39 max.
40-47
38-45
34-42
31-38
30-37
28-37
24-33
Tensile Strength Rm (KSI)
-
190 min.
170 min.
155 min.
145 min.
140 min.
135 min.
135 min.
Yield Strength 0.2%Rp (KSI)
-
170 min.
155 min.
145 min.
125 min.
115 min.
105 min.
105 min.
Percentage of Elongation A(%)
-
10 min.
10 min.
12 min.
13 min.
14 min.
16 min.
16 min.
Section Shrinkage Z(%)
-
40 min.
44 min.
45 min.
45 min.
45 min.
50 min.
50 min.

Size Ranges

Products
Diameter (mm)
Length (mm)
Rolled bar
10~95
3,000~5,700
Forged bar
95.2~600
3,000~5,700
Billet
130x130, 140x140, 150x150, 160x160
7,000 max
Flat bar
80x80 (min.)
Based on the customer needs

The product has been added to the inquiry form!

COOKIES

The website uses the browser’s cookies to give you the best user experience. The Cookies we used include the third party cookies. For more information, see our Privacyand Cookies Policies. By continuing to browse our website or closing this prompt, you agree to accept our Terms of Use of our website.

I agree

前往舊版網站
獲得完整瀏覽體驗

您所使用的裝置版本不支援新版網站的部分功能,請移轉至舊版網站獲得完整瀏覽體驗

立即前往