410/X12Cr13/S41000 | Martensite Stainless Steel

410

1.4006, S41000, SUS 410

SpecificationDIN EN 10088, ASTM A276/A276M, ASTM A479/A479M, JIS G4303, AMS 5613

It is the common Martensite Hardening stainless steel with good resistance to atmosphere corrosion. After heating treatment, it exhibits superior strength.

Quick Navigation

Introduction
Specifications

Inquiry

Introduction

Product properties

˙Good corrosion resistance

Industrial Applications

˙Bolts

˙Screws

˙Bushings

˙Nuts˙Shafts

˙Pumps

˙Valves

˙Gas turbines

Specifications

Chemical composition (wt. %)

Element

Min.

0.10

11.50

Max.

0.15

1.00

0.040

0.030

12.00

0.75

Physical Property

Density (g/cm^3)

7.8

Modulus of elasticity

Temperature (℃)

Gpa

206

500

170

Thermal Expansion Coefficient

Temperature (℃)

10^-6/℃

0~315

0~538

11.5

Thermal Conductivity

Temperature (℃)

W/m·K

100

24.9

500

28.7

Mechanical Property

Items

Annealed

Hardness

223 (HBW) max.

Tensile Strength Rm (KSI)

70 min.

Yield Strength 0.2%Rp (KSI)

40 min.

Percentage of Elongation A(%)

20 min.

Section Shrinkage Z(%)

45 min.

Hardness After Quenching (hardenability) (HRC)

35 min.

Size Ranges

Products

Diameter (mm)

Length (mm)

Rolled bar

10~95

3,000~5,700

Forged bar

95.2~680

3,000~5,700

Billet

130x130, 140x140, 150x150, 160x160

7,000 max

Flat bar

80x80 (min.)

Based on the customer needs

The product has been added to the inquiry form!

Martensite Stainless Steel bar 410/X12Cr13/S41000 – GMTC

410

Product properties

Industrial Applications

Newsletter Subscription