416/1.4005/X12CrS13/S41600 | Martensite Stainless Steel

416

1.4005, S41600, SUS 416

SpecificationDIN EN 10088, ASTM A314, ASTM A473, ASTMA582, JIS G4303

It has the highest machinability among all stainless steels/ After heating treatment, it has higher strength and hardness.

Quick Navigation

Introduction
Specifications

Inquiry

Introduction

Product properties

˙Great machinability

Industrial Applications

˙Valves

˙Pump shafts

˙Motor shafts

˙Washing machine parts

˙Gears

˙Bolts

˙Nuts

˙Studs

˙Auto screw machining parts

Specifications

Chemical composition (wt. %)

Element

Min.

0.15

12.00

Max.

0.15

1.00

1.25

0.060

0.40

13.00

0.75

Physical Property

Density (g/cm^3)

7.8

Modulus of elasticity

Temperature (℃)

Gpa

206

500

170

Thermal Expansion Coefficient

Temperature (℃)

10^-6/℃

0~315

0~538

11.5

Thermal Conductivity

Temperature (℃)

W/m·K

100

24.9

500

28.7

Mechanical Property

Items

Annealed

Hardness

223 (HBW) max.

Tensile Strength Rm (KSI)

70 min.

Yield Strength 0.2%Rp (KSI)

40 min.

Percentage of Elongation A(%)

20 min.

Section Shrinkage Z(%)

45 min.

Hardness After Quenching (hardenability) (HRC)

35 min.

Size Ranges

Products

Diameter (mm)

Length (mm)

Rolled bar

10~95

3,000~5,700

Forged bar

95.2~680

3,000~5,700

Billet

130x130, 140x140, 150x150, 160x160

7,000 max

Flat bar

80x80 (min.)

Based on the customer needs

Heat Treatment Conditions

Quenching: 955℃, air quenching