F6NM/1.4313/X3CrNiMo13-4/S41500 | Martensite Stainless Steel

F6NM

S41500

SpecificationASTM A182

F6NM is a Martensite stainless steel with addition of nickel and molybdenum that allow it to be better than 410 and 420 Martensite counterparts.

Quick Navigation

Introduction
Specifications

Inquiry

Introduction

Product properties

˙ Outstanding zero-notch ductility

˙ Outstanding weldability and corrosive resistance

Industrial Applications

˙ Shaft, compressor, hydraulic applications

Specifications

Chemical composition (wt. %)

Element

Min.

0.30

0.50

12.50

3.50

0.50

Max.

0.03

0.60

1.00

0.025

14.00

4.50

0.70

Physical Property

Density (g/cm^3)

7.75

Modulus of elasticity

Temperature (℃)

Gpa

200

500

Thermal Expansion Coefficient

Temperature (℃)

10^-6/℃

100

10.5

400

11.6

Thermal Conductivity

Temperature (℃)

W/m·K

Mechanical Property

Items

Annealed

Tensile Strength Rm

95 KSI min.

Yield Strength 0.2Rp

75 KSI min.

Yield Strength A(%)

18% min.

Yield Strength Z(%)

35% min.

Hardness

197-233 HBW

Size Ranges

Products

Diameter (mm)

Length (mm)

Rolled bar

10-95

3,000-5,700

Forged bar

95.2-680

3,000-5,700

Billet

130x130, 140x140, 150x150, 160x160

7,000 max.

Flat bar

80*80 (min.)

Based on the customer needs

Heat Treatment Conditions

Quenching: 1010°C min.

Tempering 1: 560°C min.